用户名:
@cn-txw.com
密  码:
Carbon Fabrics
Aramid Fabrics
Hybrid Fabrics
Carbon Fiber and Aramid fiber Blend Woven Cloth
Carbon Fiber Composite Cloth
Carbon Fiber Reinforcement Unidirectional Cloth
Preimpregnated Braided Carbon Fabrics
Carbon Fiber Composite Material Products
Aramid fiber Reinforcement Unidirectional Cloth
Aramid Tyre Cord Fabrics
Jiangsu Yujie Carbon Fibre Sci-Tech Co., Ltd.
Tel:0510-87892988 87891677
Fax:0510-87892677
Mobile:13801534666
Adress:Yixing, Jiangsu, China
Website:www.cn-txw.com
E-mail:yj@cn-txw.com
Preimpregnated Braided Carbon Fabrics
Read:690  2008-11-10
 



Preimpregnated Braided Carbon Fabrics

Name

 Weight (g/m2)

Resin Content(wt%) Total Weight(g/m2) Formed Thickness(mm) Type of Carbon Fiber Width of Preimpregnated Cloth(mm)
YJ-B1K-P125 125 40 208 0.138 1K 1000
YJ-B3K-T125 200 40 333 0.221 3K 1000
YJ-B3K-P125 200 40 364 0.245 3K 1000
YJ-B6K-P125 380 38 613 0.403 6K 1000
YJ-B6K-T125 330 38 550 0.364 6K 1000
YJ-B12K-P125 740 38 1210 0.794 12K 1000


Braided Carbon Fiber Cloth/130 curing general purpose epoxy

Composition Properties: Vf=60% conversion       test direction=0degree (longitudinal)

Weight Tensile Strength Tensile Modulus Bending Strength Bending Modulus Compression Strength Compression Modulus Cutting Strength
g/m2 kgf/mm2 MPa

103kgf/mm2

GPa kgf/mm2 MPa 103 kgf/mm2 GPa kgf/mm2 MPa 103 kgf/mm2 GPa kgf/mm2 MPa
200 95 930 8 75 90 880 7 65 97 65 7 65 8 80

The above data is for reference only and is not guaranteed. The density of warp and weft and width of the cloth could be made to customer requirements.

 